We’re committed to ensuring that your privacy is protected by adhering to the principles of the EU General Data Protection Regulation (GDPR). Your trust is extremely important, so we’ve updated our Privacy Policy to explain how we collect, hold and handle your personal data. Forgeway is wholly committed to the privacy and security of your personal data which we store. We will never pass your details onto a third party without your permission. By providing your details you agree to be contacted by us; and we’ll treat your data with respect. If you would prefer not to hear from us at any time you can get in touch or email: enquiries@forgeway.com

Latest News

Latest News

Environmental stress cracking

ENVIRONMENTAL STRESS CRACKING (ESC)
Are you using the correct adhesive?
Did you know that you could be unintentionally weakening your plastic? Selecting the wrong adhesive could lead to an issue called environmental stresscracking, sometimes referred to as the ‘Plastic Killer’Environmental stress cracking(ESC) is defined as the premature embrittlement and subsequent formation of cracks in plastics as a result of both being under stress and in contact with a chemical agent.
Environmental stress cracking isa significant problem, accounting for ‘25% of all plastic failure in commercial usage’[1].
In ESC a chemical agent does not cause direct molecular degradation or chemical attack, but instead permeates into the molecular structure of the plastic and weakens the forces between the polymer chains, resulting in molecular disentanglement. In short, the plastic will become severely weakened and as a  result will develop cracks and become structurally compromised.
An example of environmental stress cracking on polycarbonate can be seen below. The polycarbonate sample at the top has been placed under stress for over 7 hours with no chemical agent applied, it shows no visual signs of cracking. However, the polycarbonate on the bottom was once again placed under strain, but when a chemical agent commonly found in adhesives and paints was applied to this surface, cracksdeveloped within 10 minutes and the test piece snapped. The test piece in the middle was exposed to the same chemical agent but was not placed under any stress and no cracks were observed. This shows that you need
both a form of strain and a chemical agent to cause environmental stress cracking.
At Forgeway® we have carefully designed and tested an adhesive which will be suited for your most sensitive of applications. So, if you have plastic under strain and want to use an adhesive choose Formoa® 206i.
Stress Cracking is seen widely in the RV market as plastic is used extensively and is often placed under strain during every day life.
[1]: J. A. Jansen, “Environmental stress cracking: the plastic killer,” Advanced Materials and Processes, vol. 162, no. 6, pp. 50–53, 2004.
Case Study | Environmental Stress Cracking (ESC)

Topics: Adhesives

   

Subscribe to our newsletter

We’re committed to ensuring that your privacy is protected by adhering to the principles of the EU General Data Protection Regulation (GDPR). Your trust is extremely important, so we’ve updated our Privacy Policy to explain how we collect, hold and handle your personal data. Forgeway is wholly committed to the privacy and security of your personal data which we store. We will never pass your details onto a third party without your permission. By providing your details you agree to be contacted by us; and we’ll treat your data with respect. If you would prefer not to hear from us at any time you can get in touch or email: enquiries@forgeway.com